MKETTLE – HARD ANODISED
The world's most compact double walled kettle- The mKettle! The mKettle is proven in the field and recommended by outdoor enthusiasts who are used to cycling, canoeing/kayaking, camping, fishing, or backpacking light where weight, size, and function are critical. Composition: Hard Anodized Aluminium, British Standard ISO10074:2010 Weight: 370g (13 oz) Capacity: 530 ml (18 oz) Approximately 1 pint Dimensions: 17cm (7”) Tall by 10cm (3.75”) Diameter Pack: Fitted rip stop nylon carry bag with D-Rings Fuel: Solid, eco-friendly, no gas-canisters required; Successfully paired with Trangia (Sweden), White Box (USA), and Evernew (Japan) Spirit Burners. Transport: Use stopper to carry water Storage: There is adequate space for matches and a fire Starter inside fire base
“HARD ANODIZING” EXPLAINED
The Result of Hard Anodising is that you get a thicker stronger coating which is approximately 2-4 times stronger than the normal Anodising process. It’s as close as you can get to titanium while still using an easily machinable aluminum and stronger than stainless steel, with the added benefits of being lighter (a necessity when camping or travelling long distances) boiling water quicker and, importantly, unlike stainless steel, it won’t rust!
All of our Anodised Kettles use the Hard Anodisation process, and the Ghillie Kettle company are proud to say that this is the most durable kettle to date.
Anodisation is primarily used to toughen up the outer shell of the aluminum and is also an easy way to add color to your piece. What the process actually does is creates a aluminium hydroxide layer on the surface of the metal. After the process is complete the aluminum is no longer susceptible to nicks and scratches to the surfaces because the pores of the metal have tightened up creating a harder surface.
There are 3 types of Anodisation
- Type I – is a specialist anodising using chromic or phosphoric acid instead of sulphuric acid,.
- Type II – is the Anodising that can be done in a garage, using sulfuric acid and coloured dyes.
- Type III – is hard coat Anodisation, or Hard Anodising. Requires a more controlled environment.
Type III or Hard Anodising is performed with a weaker solution of sulfuric acid, and a lower temperature acid bath. Normally for Type II anodising we have our acid bath around 60-70 degrees fahrenheit. The temperature often rises during the anodising process. For type III hard Anodising, the temperature must be at 35-40 degrees. The acid bath must be constantly mixed, otherwise a warm layer of acid will build up around the piece. The electric current will be much higher, perhaps 20 amps per sq foot. This requires bath mixing machines and cooling equipment.